1·Scatter and fracture surface roughness increases with loading rate.
分散性和断裂表面的粗糙度随加载率而提高。
2·The fatigue fracture surface features of blade are summarized firstly.
归纳总结了叶片疲劳断口的特征形貌。
3·The fracture surface traverses matrix as well as fibers and interface .
断裂表面横切过基体、纤维和界面。
4·Quenching crack deep and long, straight fracture, fracture surface without oxide color.
淬火裂纹深而细长，断口平直，破断面。
5·Fracture surface consists of plastic yield deformation area and elastic deformation area.
断口主要分为塑性屈服变形区和弹性变形区两部分。
6·The fracture surface appeared intergranular crack, due to the oxide formed during tensile test.
拉伸过程中形成的氧化物夹杂成为裂纹源，断口表现为沿晶断裂。
7·Fractal dimension of impact fracture surface of 08f steel was measured by vertical section method.
利用垂直截面法测量了08f钢经不同形变氮化复合后冲击断裂表面的分形维数。
8·The adiabatic heating induces the temperature of fracture surface layer to be higher than the liquidus temperature too.
计算表明， 断口表面层绝热升温温度依然高于液相线温度。
9·The cause has been analyzed which makes a difference of anti - destroying property and fracture surface feature of chrome clad.
对两种状态铬层的破坏抗力差异和端面形貌特征的形成原因进行了分析。
10·The fracture surface of a failed injection valve nut of diesel engine high pressure oil pump was investigated by visual and SEM.
对断裂的汽车柴油机高压出油阀紧座的宏观、微观断口及显微组织进行了研究。
1·Many round voids which result in stress concentration easily are found on SEM micrographs of fracture surface after heat-treatment, so the notched izod impact strength of the sample decreases.
由热处理后试样冲击断面的SEM照片可见水分挥发留下的空洞，这些空洞容易形成应力集中点，因而导致冲击韧性降低。
2·In measurement of data on rock fracture surface, some errors will certainly occur. These errors will make the fractal interpolation curves (surfaces) have some deviations.
在岩石断面数据点的实际测量过程中，必然会产生一些误差，而这些误差又必然会引起分形插值曲线(曲面)的偏离。
3·The mechanical property and processing property of soft PVC/ABS alloy were tested, the fracture surface structure of the sample and compatibility of the two phases were characterized.
前言： 对软质聚氯乙烯（ PVC）/ 丙烯腈-丁二烯-苯乙烯共聚物（ ABS） 合金的力学性能、加工性能进行了测试，并利用差示扫描量热仪和扫描电镜对试样断面结构以及两相的相容性进行了表征。