1·The corrosion of poor Cu area is the root of intergranular corrosion.
贫铜区受到腐蚀是晶间腐蚀的根源。
2·The reason of intergranular corrosion and exfoliation corrosion is analyzed.
分析了发生晶间腐蚀和剥蚀的原因。
3·There is mainly intergranular corrosion with different extent on Cu-Ni alloys in marine.
各海域对铜镍合金的腐蚀作用基本均以沿晶腐蚀为主， 但程度不同；
4·The results showed that above cracks are intergranular corrosion cracking basically in weak oxidative medium;
结果表明，裂纹基本属于弱氧化性介质条件下的晶间腐蚀开裂；
5·The results show that both of two elements additions can improve the intergranular corrosion resistance of Zine-base alloys.
结果表明，两种元素皆可提高锌基合金的抗晶间腐蚀能力；
6·The corrosion behavior of 2d12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.
对不同规格2d 12铝合金进行晶间腐蚀、剥蚀和应力腐蚀性能测定。
7·The results show that the cracking of pigtail tubes is brittle cracking caused by creep holes and terrible intergranular corrosion.
结果表明，猪尾管道开裂为沿晶脆性开裂，长期高温服役产生的蠕变孔洞及严重的晶间腐蚀共同导致了该管道的开裂。
8·The Intergranular corrosion properties of cast aluminum alloy A356.0 are studied. The organizational reasons of corrosion are analysed.
对铸造铝合金a356.0晶间腐蚀性能进行研究，分析了产生腐蚀的组织原因。
9·Intergranular corrosion for diffusion bonded joints and base materials of 316l stainless steel was investigated by double loop EPR test.
采用双环电化学动电位再活化法(EPR法)研究316l奥氏体不锈钢扩散连接试样与母材的晶间腐蚀行为。
10·Because the welding is affected by sensitive temperature, the intergranular corrosion resistance of weld metal is worse than that of base metal.
由于焊接过程中受到敏化温度影响，焊缝的耐晶间腐蚀性要比母材差。